    Organopolysilazane (room temperature curing coating resin) IOTA-OPSZ-9150

    The product has a unique Si-NH-Si bond, can be cured at room temperature, curing mainly involved in the reaction of Si-NH-Si hydrolysis and oxidation. While the Si-NH-Si bond and the substrate surface-OH easily react, and bring the substrate and good adhesion. Addition the appropriate catalyst in the resin can promote Si-H and Si-NH-Si reaction, after curing resin to form three-dimensional cross-linked structure, giving the material good mechanical properties, hardness can be as high as 9H.

    IOTA OPSZ-9150 is a transparent, batch-stable preparation new polysilazane resin, the structure is as follows:

    OPSZ-9150 can anti-alcohol, ketones and other organic solvents after curing with.
    OPSZ-9150 is a transparent solid after curing.

    OPSZ-9150 is a one-component product. It is soluble in polar and non-polar solvents, such as ethers and alkanes, but can’t be diluted with alcohol solvents or water.



    Room temperature curing
    Non-combustible (after curing)

    Good persistence

    Easy to clean
    Anti-oxidation, anti-corrosion

    Construction convenient


    Appearance: colorless transparent liquid

    Auxiliary content: 1.5%
    Solid content: 100%

    Viscosity: 50 cPs
    Density after curing: 1.3 g / ml

    Liquid density: 0.95 g / ml

    Dry time: 2 hours

    Fully cured (20-25 ° C): 3 days

    Hardness after curing:

    Room temperature curing for 1 day: 4H

    Room temperature curing for 3 days: 6H

    Room temperature 3 hours, 120 degrees 2h: 8H

    Transmittance (visible light):> 90%

    Water contact angle: 105 °

    Metal adhesion (grid method): 0 level


    Anti-graffiti building, metal anti-corrosion coating
    Ordinary organic resin hardening agent

    Silicone curing agent


    5 liters metal sealed drum.


    Proper cleaning is important. After using, promptly use acetone or solvent oil to wipe the tool cleaning.

    OPSZ-9150 cured, ordinary solvents can’t be washed away. Can be used strong alkali, such as sodium hydroxide 10% aqueous solution soak for 5 hours or more to remove.


    In a ventilated, dry environment, and use the necessary protective measures, such as gloves, masks, goggles.

    Do not place uncured OPSZ-9150 near to fire, humid air, or water.

    After opening, seal it in a timely manner. If it is used in a humid environment, replace the container with nitrogen after using.


    Shelf life: 2years; after the application, it depend on the protective measures, sealed low temperature drying case, the applicable period of more than half a year.

Telephone:015255260163 Mobile:0086-15255260163