In the field of high - temperature coatings, IOTA OPSZ 1800 organosilicon polysilazane heat - curing coating resin stands out as an exceptional choice.

It boasts an extraordinary high - temperature resistance. The coating can withstand working temperatures of up to 1000 +°C, and its peak service temperature can reach 1800°C, providing long - lasting high - temperature protection for objects. It adopts a low - viscosity solvent - free system with a solid content of 99.99%, which is both environmentally friendly and efficient. Heating it to 200°C enables rapid curing. If free - radical initiators such as dicumyl peroxide are added, the curing temperature can be reduced. Within the temperature range of 100°C to 180°C, curing can be completed in 1 to 90 minutes, significantly improving construction efficiency.

For high - temperature formulations, heating the coated object to 425°C can promote the conversion of the polymer into ceramic, and heating above 700°C yields even better results, making it suitable for manufacturing high - temperature ceramic coatings. It is also an ideal material for heat - stable anti - corrosion coatings and non - stick coatings.

In terms of formulation and application, the typical dosage is 10 - 60%, and it is compatible with various solvents including alkanes, aromatic hydrocarbons, ethers, ketones, and esters. Its coating performance is excellent, with a variety of colors, gloss levels ranging from matte to satin, a thickness of 10 - 300μm, a pencil hardness of >9H, and good chemical resistance and heat - shock resistance.

Whether in the aerospace, automotive manufacturing, or industrial furnace industries, IOTA OPSZ 1800 can meet the stringent requirements for high - temperature protection and special coatings with its outstanding performance. Choose IOTA OPSZ 1800 for a reliable, efficient, and high - quality high - temperature coating solution!

Room termperature curing polysilazane, pls check IOTA 9150, IOTA 9150K.       
High termperature curing polysilazane, pls check IOTA 9108, IOTA 9118.